Volume 7, Issue 4, December 2018, Page: 111-117
Role of [Cu]/[In] Molar Ratio in Controlling Structural, Morphological and Optical Properties of Sprayed CuInS2 Thin Films
Mazabalo Baneto, Department of Physics, University of Lomé, Lomé, Togo
Damgou Mani Kongnine, Department of Physics, University of Lomé, Lomé, Togo
Krishnasamy Ravichandran, Post Graduate and Research Department of Physics, AVVM Sri Pushpam College (Autonomous), Thanjavur, India
Donafolgo Soro, Department of Sciences and Technology, High Normal School of Abidjan, Abidjan, Ivory Coast
Koffi Sagna, Department of Physics, University of Lomé, Lomé, Togo
Kossi Napo, Department of Physics, University of Lomé, Lomé, Togo
Received: Oct. 25, 2018;       Accepted: Nov. 10, 2018;       Published: Dec. 18, 2018
DOI: 10.11648/j.am.20180704.13      View  41      Downloads  12
Abstract
CuInS2 thin films were deposited by chemical spray pyrolysis from aqueous solutions containing CuCl2, InCl. and thiourea at substrate temperature of 300°C and annealed at 500°C in air. [Cu]/[In] molar ratio was varied from 0.8 to 1.4 in precursor solution. The influence of [Cu]/[In] molar ratio on structural, morphological and optical properties of CuInS2 thin films was investigated. X-ray diffraction analysis shows that all the films have chalcopyrite structure with the preferential orientation along (112) plane. CuInS2 films with indium excess have poor crystallinity and consist of large quantity of small particles while copper-rich films exhibit good crystallinity with large grains. The best film crystallinity is obtained for [Cu]/[In] = 1.2. The scanning electron microscopy and atomic force microscopy images indicated that [Cu]/[In] molar ratio has a strong influence on the microstructure and surface morphology of the films. It was observed that films obtained with [Cu]/[In] ratio of 0.8 are porous. But films surface became gradually dense with increase in [Cu]/[In] molar ratio. As consequence films roughness decreased from 236.12 nm to 110.30 nm. Optical analysis shows that all the films have good absorbance in the visible. The optical absorbance of films is found to increase with increase in [Cu]/[In] molar ratio.
Keywords
Thin Film, CuInS2, Molar Ratio, Spray Pyrolysis
To cite this article
Mazabalo Baneto, Damgou Mani Kongnine, Krishnasamy Ravichandran, Donafolgo Soro, Koffi Sagna, Kossi Napo, Role of [Cu]/[In] Molar Ratio in Controlling Structural, Morphological and Optical Properties of Sprayed CuInS2 Thin Films, Advances in Materials. Vol. 7, No. 4, 2018, pp. 111-117. doi: 10.11648/j.am.20180704.13
Copyright
Copyright © 2018 Authors retain the copyright of this article.
This article is an open access article distributed under the Creative Commons Attribution License (http://creativecommons.org/licenses/by/4.0/) which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.
Reference
[1]
Park MS, Han SY, Bae EJ, Lee TJ, Chang CH, Ryu SO, Synthesis and characterization of polycrystalline CuInS2 thin films for solar cell devices at low temperature processing conditions, Curr Appl Phys 2010; 10: S 379–82.
[2]
I. Konovalov, Material requirements for CIS solar cells, Thin Solid Films 451– 452 (2004) 413–419.
[3]
R. S. Singh, V. K. Rangari, S. Sanagapalli, V. Jayaraman, S. Mahendra, V. P. Singh, Nano structured CdTe, CdS and TiO2 for thin film solar cell applications, Sol. Energy Mater. Sol. Cells 82 (2004) 315–330.
[4]
C. Lévy-Clément, R. Tena-Zaera, M. A. Ryan, A. Katty, G. Hodes, CdSe - sensitized p-CuS CN/nanowire n- ZnO heterojunctions, Adv. Mater. 17 (2005) 1512–1515.
[5]
M. Biancardo, F. C. Krebs, Micro structured extremely thin absorber solar cells, Sol. Energy Mater. Sol. Cells 91 (2007) 1755–1762.
[6]
I. M. Dharmadasa, R. P. Burton, M. Simmonds, Electrodeposition of CuInSe2 layers using a two-electrode system for applications in multi-layer graded bandgap solar cells, Sol. Energy Mater. Sol. Cells 90 (2006) 2191–2200.
[7]
A. M. Martinez, A. M. Ferna´ndez, L. G. Arriaga, U. Cano, Preparation and characterization of Cu–In–S thin films by electrodeposition, Mater. Chem. Phys. 95 (2006) 270–274.
[8]
J. Bekker, V. Alberts, A. W. R. Leitch, J. R. Botha, Properties of CuIn (Se, S) 2 thin films prepared by two-step growth processes, Thin Solid Films 431–432 (2003) 116–121.
[9]
M. Venkatachalam, M. D. Kannan, S. Jayakumar, R. Balasundaraprabhu, A. K. Nandakumar, N. Muthukumarasamy, CuInxGa1xSe2 thin films prepared by electron beam evaporation, Sol. Energy Mater. Sol. Cells 92 (2008) 571–575.
[10]
J. Palm, V. Probst, F. H. Karg, Second generation CIS solar modules, Sol. Energy 77 (2004) 757–765.
[11]
J. M. Meese, JC Manthuruthil, D. R. Locker, CuInS2 Diodes for solar energy conversion, Bull Am Phys Soc 1975; 20:696–707.
[12]
P. Guha, S. Gorai, D. Ganguli, S. Chaudhuri, Ammonia‐mediated wet chemical synthesis of CuInS2 Mater Lett 2003; 57:1786–1791.
[13]
W. J. Tsai, C. H. Tsai, C. H. Chang, J. M. Ting, R. R. Wang, Addition of Na into CuInS2 thin film via co- evaporation Thin Solid Films 2010; 519: 1712–1716.
[14]
J. P. Xiao, Y. Xie, R. Tang, Y. T. Qian, Synthesis and Characterization of Ternary CuInS2 Nanorods Via a Hydrothermal Route, J Solid State Chem 2001; 161: 179–183.
[15]
Y. Chen, X. He, X. Zhao, M. Song, X. Gu, Preparation and characterization of copper indium disulfide films by facile chemical method, Mater. Sci. Eng. B 139 (2007) 88–94.
[16]
K. Siemer, J. Klaer, I. Luck, J. Bruns, R. Klenk, D. Braünig, Efficient CuInS2 solar cells from a rapid thermal process (RTP), Sol. Energy Mater. Sol. Cells 67 (2001) 159– 166.
[17]
R. Scheer, I. Luck, M. Kanis, M. Matsui, T. Watanabe, T. Yamamoto, Incorporation of the doping elements Sn, N, and P in CuInS2 thin films prepared by co-evaporation, Thin Solid Films 392 (2001) 1.
[18]
H. J. Muffer, C. H. Fischer, K. Diesner, LGAR—A novel thin-film technology for sulfides, Sol. Energy Mater. Sol. Cells 67 (2001) 121.
[19]
J. A. Hollingsworth, K. K. Banger, M. H. C. Jin, Single source precursors for fabrication of I-III-VI2 thin-film solar cells via spray CVD), Thin Solid Films 431 (2003) 63.
[20]
M. Baneto, A. Enesca, C. Mihoreanu, Y. Lare, K. Jondo, K. Napo, A. Duta, Effects of the growth temperature on the properties of spray deposited CuInS2 thin films for photovoltaic applications. Ceramics International 41 (3), 4742-4749 (2015).
[21]
Y. B. He, A. Polity, H. R. Alves, I. O¨ sterreicher, W. Kriegseis, D. Pfisterer, B. K. Meyer, M. Hardt, Structural and optical characterization of RF reactively sputtered CuInS2 thin films, Thin Solid Films 403– 404 (2002) 62.
[22]
H. M. Pathan, C. D. Lokhande, Chemical deposition and characterization of copper indium disulphide thin film, Appl. Surf. Sci. 239 (2004) 11.
[23]
M. Baneto, A. Enesca, Y. Lare, K. Jondo, K. Napo, A. Duta, Effect of precursor concentration on structural, morphological and opto-electric properties of ZnO thin films prepared by spray pyrolysis Ceramics International 40 (2014) 8397–8404.
[24]
A. Enesca, M. Baneto, D. Perniua, L. Isaca, C. Bogatu, A. Duta, 7. Solar-activated tandem thin films based on CuInS2, TiO2 and SnO2 in optimized wastewater treatment processes, Applied Catalysis B: Environmental 186 (2016) 69–76.
[25]
J. H. Schon, E. Bucher, Characterization of Intrinsic Defect Levels in CuInS2, Phys. Status Solidi 171 (1999) 511.
[26]
M. Krunks, V. Milli, O. Bijakina, H. Rebane, Composition and structure of CuInS2 films prepared by spray pyrolysis, Thin Solid Films 361 (2000) 61.
[27]
G. C. Park, H. D. Chung, C. D. Kim, H. R. Park, W. J. Jeong, J. U. Kim, H. B. Gu, K. S. Lee, Photovoltaic characteristics of CuInS2/CdS solar cell by electron beam evaporation, Solar Energy Materials and Solar Cells 49 (1997) 365.
[28]
R. Klenk, T. Walter, H. W. Schock, A model for the successful growth of polycrystalline films of CuInSe2 by multisource physical vacuum evaporation, Adv. Mater. 5 (1993) 114.
[29]
S. B. Zhang, S. H. Wei, A. Zuger, Defect physics of the CuInSe2 chalcopyrite semiconductor Phys. Rev. 57 (1997) 9642.
Browse journals by subject